Alloy Nominal Compositions
Corrosion-resistant alloys:
Nickel-Base:
Alloy |
Nia |
Co | Fe | Cr | Mo | W | Mn | Si | Cb | V | Al | Ti | C | Cu | Others |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
B-2 | 69 | 1* | 2* | 1* | 28 | 0.5* | 1* | 0.1* | – | – | – | – | 0.01* | 0.5* | – |
B-3® |
65b |
3* | 1.5 | 1.5 | 28.5 | 3* | 3* | 0.1* | 0.2* | 0.2* | 0.5* | 0.2* | 0.01* | 0.2* | Ta-0.2*, Zr-0.01* |
C-4 | 65 | 2* | 3* | 16 | 16 | – | 1 | 0.08* | – | – | – | 0.7* | 0.01* | 0.5* | – |
C-22® | 56 | 2.5* | 3 | 22 | 13 | 3 | 0.5* | 0.08* | – | 0.35* | – | – | 0.01* | 0.5* | – |
C-22HS® | 61 | 1* | 2* | 21 | 17 | 1* | 0.8* | 0.08* | – | – | 0.5* | – | 0.01* | 0.5* | – |
C-86 | 58 | – | 5* | 21 | 16 | 4 | 1* | 0.08* | – | – | 0.5* | 0.25* | 0.01* | 0.5* | – |
C-276 | 57 | 2.5* | 5 | 16 | 16 | 4 | 1* | 0.08* | – | 0.35* | – | – | 0.01* | 0.5* | – |
C-2000® | 59 | 2* | 3* | 23 | 16 | – | 0.5* | 0.08* | – | – | 0.5* | – | 0.01* | 1.6 | – |
G-30® | 43 | 5* | 15 | 30 | 5.5 | 2.5 | 1.5* | 0.8* | 0.8 | – | – | – | 0.03* | 2 | – |
G-35® | 58 | 1* | 2* | 33.2 | 8.1 | 0.6* | 0.5* | 0.6* | – | – | 0.4* | – | 0.05* | 0.3* | – |
G-50® |
50b |
2.5* | 17 | 20 | 9 | 1* | 1* | 1* | 0.5* | – | 0.4* | – | 0.02* | 0.5* | – |
HYBRID-BC1® | 62 | 1* | 2* | 15 | 22 | – | 0.25 | 0.08* | – | – | 0.5* | – | 0.01* | – | – |
N | 71 | 0.2* | 4* | 7 | 16 | 0.5* | 0.8* | 1* | – | 0.5* | – | – | 0.06 | 0.35* | (Al+Ti)-0.5* |
aAs balance bMinimum cCb+Ta *Maximum
Cobalt-Base:
Alloy |
Coa |
Ni | Fe | Cr | Mo | W | Mn | Si | N | C |
---|---|---|---|---|---|---|---|---|---|---|
ULTIMET® | 54 | 9 | 3 | 26 | 5 | 2 | 0.8 | 0.3 | 0.08 | 0.06 |
aAs balance bMinimum cCb+Ta *Maximum
High-temperature Alloys:
Nickel-Base:
Alloy |
Nia |
Co | Fe | Cr | Mo | W | Mn | Si | Cb | Al | Ti | C | B | Zr | Cu | Others |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
75 | 76 | – | 5* | 20 | – | – | 1* | 1* | – | 0.4* | 0.4 | 0.11 | – | – | 0.5* | – |
214® | 75 | 2* | 3 | 16 | 0.5* | 0.5* | 0.5* | 0.2* | 0.15* | 4.5 | 0.5* | 0.04 | 0.01* | 0.1* | – | Y-0.01 |
230® | 57 | 5* | 3* | 22 | 2 | 14 | 0.5 | 0.4 | 0.5* | 0.3 | 0.1* | 0.1 | 0.015* | – | 0.5* | La-0.02 |
233® | 48 | 19 | 1.5* | 19 | 7.5 | 0.3* | 0.4* | 0.20* | – | 3.3 | 0.5 | 0.1 | 0.004 | 0.03 | – | Ta-0.5,Y-0.025* |
242® | 65 | 1* | 2* | 8 | 25 | – | 0.8* | 0.8* | – | 0.5* | – | 0.03* | 0.006* | – | 0.5* | – |
244® | 61 | 1* | 2* | 8 | 22.5 | 6 | 0.8* | 0.1* | – | 0.5* | – | 0.03* | 0.006* | – | – | – |
263 | 52 | 20 | 0.7* | 20 | 6 | – | 0.4 | 0.2 | – | 0.6* | 2.4* | 0.06 | 0.005* | 0.04* | 0.2* | (Al+Ti)-2.6 |
282® | 57 | 10 | 1.5* | 20 | 8.5 | – | 0.3* | 0.15* | – | 1.5 | 2.1 | 0.06 | 0.005* | – | – | – |
617 | 54 | 12.5 | 1 | 22 | 9 | – | 0.2* | 0.2* | – | 1.2 | 0.3 | 0.07 | 0.006* | – | – | – |
625 | 62 | 1* | 5* | 21 | 9 | – | 0.5* | 0.5* |
3.7c |
0.4* | 0.4* | 0.1* | – | – | 0.5* | – |
625SQ® | 62 | 1* | 5* | 21 | 9 | – | 0.5* | 0.15* |
3.7c |
0.4* | 0.4* | 0.03* | – | – | 0.5* | N-0.02* |
718 | 52 | 1* | 19 | 18 | 3 | – | 0.35* | 0.35* | 5c | 0.5 | 0.9 | 0.05 | – | 0.004 | 0.1* | – |
B | 67 | 2.5* | 5 | 1* | 28 | – | 1* | 1* | – | – | – | 0.05* | – | – | 0.15* | V-0.3 |
HR-160® | 37 | 29 | 2* | 28 | 1* | 1* | 0.5 | 2.75 | 1* | 0.4* | 0.5 | 0.05 | – | – | 0.5* | – |
HR-224® | 47 | 2* | 27.5 | 20 | 0.5* | 0.5* | 0.5* | 0.3 | 0.15* | 3.8 | 0.3 | 0.05 | 0.004* | 0.025* | – | – |
HR-235® | – | – | 1.5* | 31 | 5.6 | – | 0.65* | 0.6* | 1* | 0.4* | 0.5* | 0.06* | – | – | 3.8 | – |
R-41 | 52 | 11 | 5* | 19 | 10 | – | 0.1* | 0.5* | – | 1.5 | 3.1 | 0.09 | 0.006 | 0.07* | – | – |
S | 67 | 2* | 3* | 16 | 15 | 1* | 0.5 | 0.4 | – | 0.25 | – | 0.02* | 0.015* | – | 0.35* | La-0.02 |
W | 63 | 2.5* | 6 | 5 | 24 | 1* | 1* | 1* | – | – | – | 0.12* | – | – | 0.5* | V-0.6* |
Waspaloy | 58 | 13.5 | 2* | 19 | 4.3 | – | 0.1* | 0.15* | – | 1.5 | 3 | 0.08 | 0.006* | 0.05 | 0.1* | – |
X | 47 | 1.5 | 18 | 22 | 9 | 0.6 | 1* | 1* | 0.5* | 0.5* | 0.15* | 0.1 | 0.008* | – | 0.5* | – |
X-750 |
70b |
1* | 8 | 16 | – | – | 0.35* | 0.35* | 1c | 0.8 | 2.5 | 0.08* | – | – | 0.5* | – |
aAs balance bMinimum cCb+Ta *Maximum
Cobalt-Base:
Alloy |
Coa |
Ni | Fe | Cr | Mo | W | Mn | Si | Cb | Al | Ti | C | B | Zr | Cu | Others |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
6B | 58 | 2.5 | 3* | 30 | 1.5* | 4 | 1.4 | 0.7 | – | – | – | 1 | – | – | – | – |
25 | 51 | 10 | 3 | 20 | 1* | 15 | 1.5 | 0.4* | – | – | – | 0.10 | – | – | – | – |
188 | 39 | 22 | 3* | 22 | – | 14 | 1.25* | 0.35 | – | – | – | 0.10 | 0.015* | – | – | La-0.03 |
NS-163® | 40 | 8 | 21 | 28 | – | – | 0.5* | 0.5* | 1 | 0.5* | 1.3 | 0.10 | 0.015* | – | 0.2* | – |
aAs balance bMinimum cCb+Ta *Maximum
Iron-Base:
Alloy |
Fea |
Ni | Co | Cr | Mo | W | Mn | Si | Cb | Ta | Al | C | N | B | Cu | Others |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
556® | 31 | 20 | 18 | 22 | 3 | 2.5 | 1 | 0.4 | 0.3* | 0.6 | 0.2 | 0.1 | 0.2 | 0.02* | – | Zr-0.02, La-0.02 |
HR-120® | 33 | 37 | 3* | 25 | 1* | 0.5* | 0.7 | 0.6 | 0.7 | – | 0.1 | 0.05 | 0.2 | 0.004 | 0.5* | Ti-0.2* |
MULTIMET® | 30 | 20 | 20 | 21 | 3 | 2.5 | 1.5 | 1* | 1c | – | – | 0.12 | 0.15 | – | 0.5* | – |
aAs balance bMinimum cCb+Ta *Maximum
Titanium Alloys:
Alloy |
Tia |
Al | V | Fe | Sn | Cr | C | N | O | H |
---|---|---|---|---|---|---|---|---|---|---|
Ti-3Al-2.5V | 94 | 3 | 2.5 | 0.25* | – | – | 0.05* | 0.02* | 0.12* | ** |
aAs balance bMinimum cCb+Ta *Maximum **Varies with specifications