HAYNES® R-41 Sheet, Age-Hardened*
Temperature |
Creep |
Approximate Initial Stress to Produce Specified Creep in |
100h |
1,000h |
°F |
°C |
% |
ksi |
MPa |
ksi |
MPa |
1200 |
649 |
1 |
105 |
724 |
84 |
579 |
R |
110 |
758 |
90 |
621 |
1300 |
704 |
1 |
75 |
517 |
59 |
407 |
R |
85 |
586 |
68 |
469 |
1400 |
760 |
1 |
53 |
365 |
34 |
234 |
R |
63 |
434 |
43 |
296 |
1500 |
816 |
1 |
32 |
221 |
18 |
124 |
R |
39 |
269 |
24 |
165 |
1600 |
871 |
1 |
17 |
117 |
9.0 |
62 |
R |
23 |
159 |
13 |
90 |
1700 |
927 |
1 |
8.4 |
58 |
4.6 |
32 |
R |
13 |
90 |
6.5 |
45 |
*Samples were age hardened by heat treating at 2050°F (1121°C) /30 min./RAC + 1650°F (899°C) /4h/AC