HAYNES 625 Sheet, Solution Annealed
Temperature |
Creep |
Approximate Initial Stress to Produce Specified Creep in |
10 h |
100 h |
1,000 h |
°F |
°C |
% |
ksi |
MPa |
ksi |
MPa |
ksi |
MPa |
1100 |
593 |
0.5 |
75 |
517 |
69 |
476 |
64 |
441 |
1 |
76 |
524 |
71 |
490 |
67 |
462 |
R |
- |
- |
90 |
621 |
80 |
552 |
1200 |
649 |
0.5 |
53 |
365 |
52 |
359 |
50 |
345 |
1 |
58 |
400 |
53 |
365 |
51 |
352 |
R |
84 |
579 |
74 |
510 |
55 |
379 |
1300 |
704 |
0.5 |
33 |
228 |
30 |
207 |
26 |
179 |
1 |
36 |
248 |
31 |
214 |
27 |
186 |
R |
68* |
469* |
49 |
338 |
33 |
228 |
1400 |
760 |
0.5 |
18.4 |
127 |
13.0 |
90 |
9.7 |
67 |
1 |
20 |
138 |
14.5 |
100 |
11.5 |
79 |
R |
41 |
283 |
27 |
186 |
17.8 |
123 |
1500 |
816 |
0.5 |
9.7 |
67 |
5.7 |
39 |
3.2 |
22 |
1 |
11.3 |
78 |
7.0 |
48 |
4.2 |
29 |
R |
24 |
165 |
15.2 |
105 |
9.9 |
68 |
1600 |
871 |
0.5 |
5.2 |
36 |
2.6 |
18 |
1.2 |
8.3 |
1 |
6.2 |
43 |
3.3 |
23 |
1.6 |
11 |
R |
14.0 |
97 |
8.0 |
55 |
4.2 |
29 |
1700 |
927 |
0.5 |
2.6 |
18 |
1.1 |
7.6 |
- |
- |
1 |
3.4 |
23 |
1.7 |
12 |
- |
- |
R |
8.0* |
55* |
4.3 |
30 |
2.7 |
19 |
1800 |
982 |
0.5 |
1.2 |
8.3 |
- |
- |
- |
- |
1 |
1.7 |
12 |
0.5 |
3.4 |
- |
- |
R |
4.1 |
28 |
2.6 |
18 |
1.4 |
10 |
*Significant extrapolation