Tensile Data

Elevated temperature tensile tests for sheet were performed with a strain rate that is no longer standard.  These results were from tests with a strain rate of 0.005 in./in./minute through yield and a crosshead speed of 0.5 in./minute for every inch of reduced test section from yield through failure.  The current standard is to use a strain rate of 0.005 in./in./minute though yield and a crosshead speed of 0.05 in./minute for every inch of reduced test section from yield through failure.

Typical Short-Time Tensile Data, Wrought

Form Condition Test Temperature Ultimate Tensile Strength 0.2% Offset Yield Strength Elongation
°F °C ksi MPa psi MPa %
Sheet 0.052 in thick Heat-treated at 2150°F, RAC RT RT 116.0 800 57 393 43
1200 649 73.2 505 - - 35
1700 927 19.8 137 - - 39
1900 1038 10.0 69 - - 34
Sheet 0.063 in thick Heat-treated at 2150°F, RAC RT RT 118.1 814 58 400 49
800 427 98.0 676 42 292 54
1000 538 93.9 647 40 274 54
1200 649 73.5 507 38 259 28
1400 760 58.4 403 36 247 12
1600 871 38.8 268 30 207 15
1800 982 24.7 170 17 117 51
2000 1093 13.0 90 8 58 38
2100 1149 6.9 48 4 30 36
2200 1204 4.8 33 3 21 29
2300 1260 3.4 23 - - 19
2350 1288 2.6 18 - - 7
Plate 1/2 in thick Heat-treated at 2165°F, WQ -108 -78 137.7 949 74 513 63
-320 -196 190.2 1311 - - 53
Forging, 21 in diameter x 3 1/4 in thick Stress-relieved 2 h at 1200°F, AC RT RT 117.6 811 72 493 30
1200 649 83.0 572 49 338 25
Forged Bar 1-2 in thick Heat-treated at 2165°F, WQ RT RT 111.0 765 56 384 55*
Hot-Rolled Bar 1/2-2 in diameter Heat-treated at 2165°F, WQ RT RT 111.3 767 54 372 57*
Hot-Rolled Bar 0.242 in diameter, Cold-Reduced Heat-treated at 2150°F, RAC RT RT 115.8 798 - - 50
reduced 5% RT RT 115.0 793 77 527 40
reduced 10% RT RT 124.0 855 103 709 35
reduced 15% RT RT 135.2 932 123 845 24
reduced 20% RT RT 147.5 1017 136 935 20
reduced 25% RT RT 153.0 1055 143 986 15
reduced 30% RT RT 159.5 1100 153 1051 12
reduced 35% RT RT 174.5 1203 168 1160 10
reduced 40% RT RT 178.5 1231 176 1214 10

RAC- Rapid Air-Cooled
WQ-Water Quenched
*Elongation in 1 in
RT= Room Temperature

Typical Short-Time Tensile Data, Weldments

Welding Method and Material Condition Test Temperature Ultimate Tensile Strength Yield Strength Elongation
°F °C ksi MPa ksi MPa %
SMAW, Sheet, 0.125 in As-Welded RT RT 116.0 800 60.9 420 27
SMAW, Plate, 0.375 in RT RT 105.1 725 65.6 452 28
SMAW, Plate, 0.500 in RT RT 102.6 707 49.8 343 44
GTAW, Sheet, 0.125 in As-Welded RT RT 108.2 746 60.5 417 22
GTAW, Plate, 0.250 in RT RT 111.4 768 65.0 448 21
GTAW, Plate, 0.375 in RT RT 105.9 730 60.4 416 19