Physical Properties

Physical Property British Units Metric Units
Density RT 0.292 lb/in.3 RT 8.08 g/cm.3
Electrical Resistivity RT 43.8 µohm.in RT 111.2 µohm.cm
200°F 44.3 µohm.in 100°C 112.8 µohm.cm
400°F 45.2 µohm.in 200°C 114.7 µohm.cm
600°F 46.1 µohm.in 300°C 116.7 µohm.cm
800°F 46.9 µohm.in 400°C 118.6 µohm.cm
1000°F 47.8 µohm.in 500°C 120.6 µohm.cm
1200°F 48.3 µohm.in 600°C 122.4 µohm.cm
1400°F 48.6 µohm.in 700°C 123.1 µohm.cm
1600°F 48.9 µohm.in 800°C 123.8 µohm.cm
1800°F 49.3 µohm.in 900°C 124.5 µohm.cm
2000°F 49.6 µohm.in 1000°C 125.2 µohm.cm
2200°F 49.9 µohm.in 1100°C 125.9 µohm.cm
- - 1200°C 126.7 µohm.cm
Thermal Diffusivity RT 4.6 x 10-3 in2/s RT 29.4 x 10-3 cm2/s
200°F 4.8 x 10-3 in2/s 100°C 30.8 x 10-3 cm2/s
400°F 5.2 x 10-3 in2/s 200°C 33.6 x 10-3 cm2/s
600°F 5.8 x 10-3 in2/s 300°C 37.0 x 10-3 cm2/s
800°F 6.4 x 10-3 in2/s 400°C 40.6 x 10-3 cm2/s
1000°F 7.0 x 10-3 in2/s 500°C 44.3 x 10-3 cm2/s
1200°F 7.2 x 10-3 in2/s 600°C 45.6 x 10-3 cm2/s
1400°F 7.4 x 10-3 in2/s 700°C 47.2 x 10-3 cm2/s
1600°F 7.5 x 10-3 in2/s 800°C 48.6 x 10-3 cm2/s
1800°F 7.8 x 10-3 in2/s 900°C 48.7 x 10-3 cm2/s
2000°F 8.4 x 10-3 in2/s 1000°C 50.9 x 10-3 cm2/s
2200°F 8.8 x 10-3 in2/s 1100°C 54.1 x 10-3 cm2/s
- - 1200°C 56.1 x 10-3 cm2/s
Thermal Conductivity RT 75 Btu.in/h.ft2.°F RT 10.9 W/m-°C
200°F 82 Btu.in/h.ft2.°F 100°C 12.0 W/m-°C
400°F 95 Btu.in/h.ft2.°F 200°C 13.6 W/m-°C
600°F 108 Btu.in/h.ft2.°F 300°C 15.4 W/m-°C
800°F 126 Btu.in/h.ft2.°F 400°C 17.6 W/m-°C
1000°F 144 Btu.in/h.ft2.°F 500°C 19.9 W/m-°C
1200°F 162 Btu.in/h.ft2.°F 600°C 21.8 W/m-°C
1400°F 178 Btu.in/h.ft2.°F 700°C 24.7 W/m-°C
1600°F 185 Btu.in/h.ft2.°F 800°C 26.1 W/m-°C
1800°F 196 Btu.in/h.ft2.°F 900°C 26.9 W/m-°C
2000°F 213 Btu.in/h.ft2.°F 1000°C 28.7 W/m-°C
2200°F 228 Btu.in/h.ft2.°F 1100°C 31.1 W/m-°C
- - 1200°C 32.9 W/m-°C
Specific Heat RT 0.110 Btu/lb.°F RT 462 J/kg-°C
200°F 0.116 Btu/lb.°F 100°C 487 J/kg-°C
400°F 0.121 Btu/lb.°F 200°C 506 J/kg-°C
600°F 0.125 Btu/lb.°F 300°C 521 J/kg-°C
800°F 0.131 Btu/lb.°F 400°C 542 J/kg-°C
1000°F 0.136 Btu/lb.°F 500°C 562 J/kg-°C
1200°F 0.151 Btu/lb.°F 600°C 597 J/kg-°C
1400°F 0.159 Btu/lb.°F 700°C 653 J/kg-°C
1600°F 0.165 Btu/lb.°F 800°C 672 J/kg-°C
1800°F 0.167 Btu/lb.°F 900°C 689 J/kg-°C
2000°F 0.171 Btu/lb.°F 1000°C 704 J/kg-°C
2200°F 0.175 Btu/lb.°F 1100°C 719 J/kg-°C
- - 1200°C 732 J/kg-
Mean Coefficient of
Thermal Expansion
78-200°F 7.2 µin/in-°F 25-100°C 13.0 µm/m-°C
78-400°F 7.6 µin/in-°F 25-200°C 13.7 µm/m-°C
78-600°F 7.9 µin/in-°F 25-300°C 14.0 µm/m-°C
78-800°F 8.1 µin/in-°F 25-400°C 14.4 µm/m-°C
78-1000°F 8.3 µin/in-°F 25-500°C 14.9 µm/m-°C
78-1200°F 8.6 µin/in-°F 25-600°C 15.5 µm/m-°C
78-1400°F 8.9 µin/in-°F 25-700°C 15.7 µm/m-°C
78-1600°F 9.2 µin/in-°F 25-800°C 16.6 µm/m-°C
78-1800°F 9.5 µin/in-°F 25-900°C 17.1 µm/m-°C
Dynamic Modulus
of Elasticity
RT 30.6 x 106 psi RT 211 GPa
100°F 30.5 x 106 psi 50°C 210 GPa
200°F 30.1 x 106 psi 100°C 207 GPa
300°F 29.6 x 106 psi 150°C 204 GPa
400°F 29.1 x 106 psi 200°C 201 GPa
500°F 28.6 x 106 psi 250°C 198 GPa
600°F 27.8 x 106 psi 300°C 193 GPa
700°F 27.1 x 106 psi 350°C 189 GPa
800°F 26.5 x 106 psi 400°C 185 GPa
900°F 26.1 x 106 psi 450°C 182 GPa
1000°F 25.6 x 106 psi 500°C 179 GPa
1100°F 25.1 x 106 psi 550°C 176 GPa
1200°F 24.4 x 106 psi 600°C 173 GPa
1300°F 23.7 x 106 psi 650°C 168 GPa
1400°F 22.9 x 106 psi 700°C 163 GPa
1500°F 22.4 x 106 psi 750°C 159 GPa
1600°F 21.7 x 106 psi 800°C 155 GPa
1700°F 21.1 x 106 psi 850°C 151 GPa
1800°F 19.8 x 106 psi 900°C 147 GPa
950°C  266 GPa 

RT= Room Temperature