Tensile Data

Average Tensile Data, Solution Heat-treated Sheet

Test Temperature Ultimate Tensile Strength 0.2% Offset
Yield Strength
Elongation
°F °C ksi MPa ksi MPa %
RT RT 104.2 718 47.5 328 46.3
1000 538 80.0 552 28.3 195 53.6
1200 649 73.5 507 27.0 186 55.0
1400 760 57.4 396 26.4 182 48.0
1600 871 32.6 225 24.7 170 67.2
1800 982 17.1 118 13.2 91 74.7
2000 1093 8.8 61 6.4 44 56.1

RT= Room Temperature

Average Tensile Data, Solution Heat-treated Plate

Test Temperature Ultimate Tensile Strength 0.2% Offset
Yield Strength
Elongation Reduction of Area
°F °C ksi MPa ksi MPa % %
RT RT 104.3 719 46.8 322 49.8 63.3
1000 538 80.4 554 26.9 186 58.7 57.7
1200 649 72.9 503 26.0 179 55.4 59.6
1400 760 59.8 412 25.6 177 51.6 65.6
1600 871 35.8 247 26.4 182 71.1 72.3
1800 892 18.6 128 14.5 100 83.6 77.4
2000 1093 9.6 66 7.4 51 84.1 69.4

RT= Room Temperature

Comparative Yield Strengths

Temperature 0.2% Yield Strength, ksi
°F  HR-120® 800H RA330 600 601
70 46.8 35 42 41 35
1000 26.9 - - - -
1200 26.0 16.9 21.5 30 25.4
1400 25.6 18.5 18.8 26 26.8
1600 26.4 18.5 15.9 11 19.2
1800 14.5 8.1 9 6 10.9
2000 7.4 3.3 - 3.1 est 5.1

HR120 Comparative Yield Strength Figure