Physical Properties

Physical Property British Units Metric Units
Density 72°F 0.297 lb/in3 22°C 8.22 g/cm3
Melting Range 2300 - 2470 °F
1260 - 1355°C
Electrical Resistivity -400°F 43.8 µm-in -250°C 16.86 µm-cm
-300°F 43.2 µm-in -200°C 16.96 µm-cm
-200°F 43.8 µm-in -150°C 17.14 µm-cm
-100°F 44.3 µm-in -100°C 17.34 µm-cm
0°F 45.0 µm-in -50°C 17.55 µm-cm
75°F 45.4 µm-in 25°C 17.87 µm-cm
Thermal Conductivity 70°F 63 Btu-in/ft.2hr.-°F 25°C 9.2 W/m-°C
200°F 76 Btu-in/ft.2hr.-°F 100°C 11.2 W/m-°C
500°F 98 Btu-in/ft.2hr.-°F 200°C 14.1 W/m-°C
1100°F 144 Btu-in/ft.2hr.-°F 600°C 20.9 W/m-°C
1200°F 151 Btu-in/ft.2hr.-°F 650°C 21.9 W/m-°C
1300°F 159 Btu-in/ft.2hr.-°F 700°C 22.8 W/m-°C
1400°F 166 Btu-in/ft.2hr.-°F 750°C 23.8 W/m-°C
1500°F 174 Btu-in/ft.2hr.-°F 800°C 24.7 W/m-°C
1600°F 182 Btu-in/ft.2hr.-°F 850°C 25.7 W/m-°C
1700°F 189 Btu-in/ft.2hr.-°F 900°C 26.7 W/m-°C
Specific Heat RT 0.116 Btu/lb.-°F RT 486 J/kg-°C
200°F 0.117 Btu/lb.-°F 100°C 487 J/kg-°C
400 °F 0.118 Btu/lb.-°F 200°C 484 J/kg-°C
600°F 0.119 Btu/lb.-°F 300°C 491 J/kg-°C
800°F 0.123 Btu/lb.-°F 400°C 507 J/kg-°C
1000°F 0.130 Btu/lb.-°F 500°C 531 J/kg-°C
1200°F 0.139 Btu/lb.-°F 600°C 564 J/kg-°C
1400°F 0.151 Btu/lb.-°F 700°C 606 J/kg-°C
1600°F 0.167 Btu/lb.-°F 800°C 657 J/kg-°C
1800°F 0.186 Btu/lb.-°F 900°C 716 J/kg-°C
2000°F 0.205 Btu/lb.-°F 1000°C 784 J/kg-°C
Mean Coefficient of Thermal Expansion 79 - 200°F 7.7 µm/in.-°F 26 - 100°C 13.9 106 m/m-°C
79 - 1000°F 8.4 µm/in.-°F 26 - 500°C 15.0 106 m/m-°C
79 - 1200°F 8.6 µm/in.-°F 26 - 600°C 15.3 106 m/m-°C
79 - 1350°F 8.8 µm/in.-°F 26 - 700°C 15.7 106 m/m-°C
79 - 1400°F 8.9 µm/in.-°F 26 - 750°C 15.9 106 m/m-°C
79 - 1500°F 8.9 µm/in.-°F 26 - 800°C 16.0 106 m/m-°C
79 - 1600°F 9.1 µm/in.-°F 26 - 850°C 16.2 106 m/m-°C
79 - 1650°F 9.1 µm/in.-°F 26 - 900°C 16.4 106 m/m-°C
79 - 1800°F 9.2 µm/in.-°F 26 - 975°C 16.6 106 m/m-°C
Dynamic Modulus
of Elasticity
RT 29.8 x 106 psi  RT 205 GPa 
200°F   29.4 x 106 psi 100°C 202 GPa
400°F   28.6 x 106 psi 200°C 198 GPa
600°F   27.8 x 106 psi 300°C 192 GPa
800°F   26.7 x 106 psi 400°C  187 GPa
1000°F   25.8 x 106 psi 500°C  180 GPa
1200°F   24.7 x 106 psi 600°C  173 GPa
1400°F   23.3 x 106 psi 700°C  165 GPa
1600°F  22.2 x 106 psi 800°C  157 GPa
1800°F  20.4 x 106 psi 900°C  148 GPa
Poisson's Ratio -108°F 0.328 -78 °C 0.328
72°F 0.320 22 °C 0.320
Magnetic Permeability RT 1.002 at 200 oersteds (15,900 A/m)

RT= Room Temperature