Form	Test Temperature		Ultimate Tensile Strength, Ksi*	Yield Strength at 0.2% Offset, Ksi*	Elongation in 2in. (50.8 mm), %
Form	°F	°C	Ultimate Tensile Strength, Ksi*	Yield Strength at 0.2% Offset, Ksi*	Elongation in 2in. (50.8 mm), %
Sheet, 0.063in. (1.6 mm)	Room		138	72	42
	200	(93)	135	58	50
	400	(204)	134	45	62
	600	(316)	130	43	75
	800	(427)	120	41	76

Plate, 1/4 - 1 1/2 in. (6.3 - 38.1 mm)	Room		148	79	36
	200	(93)	143	70	40
	400	(204)	143	55	61
	600	(316)	138	48	70
	800	(427)	133	45	70
	1000	(538)	125	38	70
	1200	(649)	99	37	66
	1400	(760)	76	39	70
	1600	(871)	51	28	77
	1800	(982)	31	16	100

Bar, 1/2 - 2 in. (12.7 - 50.8 mm)	Room		147	76	38
	200	(93)	140	70	49
	400	(204)	140	52	66
	600	(316)	132	44	77
	800	(427)	131	43	84
	1000	(538)	115	40	79

* Ksi can be converted to MPa (megapascals) by multiplying by 6.895.

Typical Room Temperature Tensile Data, Aged Material

Condition	Ultimate Tensile Strength, ksi*	Yield Strength at 0.2% Offset, ksi*	Elongation in 2 in. (50.8 mm), %

Mill Annealed	148	79	36
Aged 1000 Hrs 400°F 204°C	148	79	34
Aged 1000 Hrs 600°F 316 °C	155	80	47
Aged 1000 Hrs 800°F 427 °C	155	81	47
Aged 1000 Hrs 1000°F 538 °C	149	77	44
Aged 1000 Hrs 1200°F 649 °C	146	85	29
Aged 1000 Hrs 1400°F 760 °C	138	77	14
Aged 1000 Hrs 1600°F 871 °C	139	71	28
Aged 1000 Hrs 1800°F 982 °C	145	71	41

Typical Impact Strength, Plate

Comparative Impact Strength

Alloy	V-Notch Impact Strength Room Temperature
Alloy	ft.-lb.	Joules

ULTIMET^® alloy	130	176
HAYNES^® 6B alloy	6	8
Type 316 Stainless Steel	80	108