Test Temperature		Ultimate Tensile Strength		Yield Strength at 0.2% Offset		Elongation in 2 in. (50.8 mm)
°F	°C	Ksi	MPa	Ksi	Mpa	%

Room	Room	144.2	995	87.6	605	36.8
1000	540	125.5	865	78.9	545	40.4
1200	650	118.5	815	81.1	565	25.5
1400	760	102.0	705	78.8	645	16.3
1600	870	58.2	400	45.0	310	15.4
1800	980	15.2	105	7.8	54	61.3
2000	1095	8.4	58	3.9	27	61.0
2100	1150	4.6	32	1.8	12	89.2
2200	1205	4.4	30	1.3	9	74.8

*Average of six tests each condition

Hot-Rolled and Solution Annealed Plate, 0.500 Inches (12.7 mm) Thick*

Test Temperature		Ultimate Tensile Strength		Yield Strength at 0.2% Offset		Elongation in 2 in. (50.8 mm)
°F	°C	Ksi	MPa	Ksi	Mpa	%

Room	Room	138.9	960	82.2	565	42.8
1000	540	120.0	825	71.5	495	47.8
1200	650	114.9	790	75.9	525	33.0
1400	760	94.4	670	73.6	505	23.1
1600	870	66.4	460	50.4	345	33.6
1800	980	16.7	115	8.4	58	86.4
2000	1095	9.0	62	4.2	29	88.6
2100	1150	6.6	46	2.1	14	99.4
2200	1205	5.0	34	1.4	10	91.5

*Average of six tests each condition