| Room Temperature Tensile Data |
Form |
Annealing Temperature |
Thickness/ Diameter |
0.2% Offset Yield Strength |
Ultimate Tensile Strength |
Elongation |
|
|
°C |
°F |
mm |
in |
MPa |
ksi |
MPa |
ksi |
% |
|
Sheet |
1135 |
2075 |
3.2 |
0.125 |
348 |
50.5 |
745 |
108.0 |
59.0 |
Plate |
1121 |
2050 |
6.4 |
0.25 |
344 |
49.9 |
703 |
102.0 |
66.0 |
Plate |
1121 |
2050 |
12.7 |
0.5 |
318 |
46.1 |
689 |
100.0 |
72.0 |
Bar |
1121 |
2050 |
25.4 |
1.0 |
319 |
46.3 |
710 |
103.0 |
66.0 |
Bar |
1121 |
2050 |
63.5 |
2.5 |
338 |
49.0 |
689 |
100.0 |
68.0 |
|
| Elevated Temperature Tensile Data (Average for Plates and Bars) |
Temperature |
0.2% Offset Yield Strength |
Ultimate Tensile Strength |
Elongation |
°C |
°F |
MPa |
ksi |
MPa |
ksi |
% |
|
93 |
200 |
313 |
45.4 |
692 |
100.3 |
69.3 |
149 |
300 |
278 |
40.3 |
656 |
95.1 |
68.2 |
204 |
400 |
248 |
36.0 |
623 |
90.3 |
69.5 |
260 |
500 |
232 |
33.7 |
600 |
87.0 |
67.9 |
316 |
600 |
219 |
31.8 |
583 |
84.6 |
68.8 |
371 |
700 |
217 |
31.5 |
570 |
82.7 |
72.3 |
427 |
800 |
215 |
31.2 |
561 |
81.3 |
72.8 |
482 |
900 |
204 |
29.6 |
543 |
78.7 |
71.0 |
538 |
1000 |
194 |
28.2 |
521 |
75.5 |
72.7 |
593 |
1100 |
185 |
26.8 |
501 |
72.7 |
72.0 |
649 |
1200 |
184 |
26.7 |
483 |
70.0 |
70.2 |
|
Room Temperature Charpy V-Notch Impact Data (19.1 mm/0.75 in Plate, Annealed at 1107°C/2025°F) |
Condition |
Impact Strength |
J |
ft.lbf |
|
Annealed |
>358 |
>264 |
Annealed then Aged for 2000 h at 427°C/800°F |
>358 |
>264 |
Annealed then Aged for 2000 h at 482°C/900°F |
>358 |
>264 |
Annealed then Aged for 2000 h at 538°C/1000°F |
>358 |
>264 |
Annealed then Aged for 2000 h at 593°C/1100°F |
>358 |
>264 |
Annealed then Aged for 2000 h at 649°C/1200°F |
104 |
77 |
|