| Form |
Test Temperature |
Ultimate
Tensile Strength,
Ksi* |
Yield Strength
at 0.2% Offset,
Ksi* |
Elongation in
2in. (50.8 mm),
% |
°F
|
°C |
|
Sheet, 0.078 in.
(2.0 mm)
thick |
Room |
114.9 |
51.6 |
61 |
400 |
(204) |
100.6 |
42.0 |
59 |
600 |
(316) |
98.8 |
35.9 |
68 |
800 |
(427) |
94.3 |
32.7 |
67 |
|
Sheet, 0.094 in.
(2.4 mm) thick |
400 |
(204) |
101.0 |
39.9 |
58 |
600 |
(316) |
97.6 |
33.5 |
64 |
800 |
(427) |
93.5 |
29.7 |
64 |
|
| Sheet, 0.063 to 0.187 in.
(1.6 to 4.7 mm) thick |
400 |
(204)1 |
100.8 |
42.1 |
56 |
600 |
(316)2 |
97.0 |
37.7 |
64 |
800 |
(427)2 |
95.0 |
34.8 |
65 |
1000 |
(538)2 |
88.9 |
33.8 |
60 |
|
| Plate, 3/16 to 1 in. (4.8 to 25.4 mm) thick |
400 |
(204)3 |
98.9 |
38.2 |
61 |
600 |
(316)3 |
94.3 |
34.1 |
66 |
800 |
(427)3 |
91.5 |
32.7 |
60 |
1000 |
(538)3 |
87.2 |
32.8 |
59 |
|
Plate, 1 in.
(25.4 mm) thick |
Room
|
113.9 |
52.9 |
59 |
600 |
(316) |
96.3 |
36.2 |
63 |
800 |
(427) |
94.8 |
30.5 |
61 |
|
| * Ksi can be converted to MPa (megapascals) by multiplying by 6.895. |
|
1-Average of 25 tests.
2-Average of 34-36 tests.
3-Average of 9-11 tests. |
| |
| |