Form	Test Temperature		Ultimate Tensile Strength, Ksi*	Yield Strength at 2% Offset, Ksi*	Elongation in 2in. (50.8 mm), %
Form	°F	°C	Ultimate Tensile Strength, Ksi*	Yield Strength at 2% Offset, Ksi*	Elongation in 2in. (50.8 mm), %
Sheet, 0.028 - 0.125 in. (0.71 - 3.2 mm) thick**	Room		116	59	57
	200	(93)	110	54	58
	400	(204)	102	44	57
	600	(316)	98	42	62
	800	(427)	95	41	67
	1000	(538)	91	40	61
	1200	(649)	85	36	65
	1400	(760)	76	35	63

Plate, 1/4 - 3/4 in. (6.4 - 19.1 mm) thick***	Room		114	54	62
	200	(93)	107	49	65
	400	(204)	98	41	66
	600	(316)	95	36	68
	800	(427)	92	35	68
	1000	(538)	88	34	67
	1200	(649)	83	32	69
	1400	(760)	76	31	68

Bar, 1/2 - 2 in. (12.7 - 50.8 mm) diameter***	Room		111	52	70
	200	(93)	105	45	73
	400	(204)	96	38	74
	600	(316)	92	34	79
	800	(427)	89	31	79
	1000	(538)	84	29	80
	1200	(649)	80	28	80
	1400	(760)	72	29	77

* Ksi can be converted to MPa (megapascals) by multiplying by 6.895. Average of 10-20 tests. * Average of 16-32 tests. **** Average of 8-16 tests.

Haynes International, Inc. 800-354-0806 765-456-6012

HASTELLOY® C-22® alloy Information*