HASTELLOY^® C-2000^® alloy Information*

An extremely versatile nickel alloy resistant to corrosion in all acids and choride solutions, over wide temperature ranges.

HASTELLOY^® C-2000^® alloy Site

Principal Features

Physical Properties

Corrosion Data

Iso-Corrosion Diagrams

Mechanical Properties

Welding and Fabrication

Machining

Specifications

HASTELLOY^® C-2000^® alloy
Technical Brief

HASTELLOY^® C-2000^® alloy
Wire Information

Metallurgist Support

Sales Office Addresses

Tubular Products

Fittings & Flanges

Mechanical Properties

Room Temperature Tensile Data

Form	Annealing Temperature		Thickness/ Diameter		0.2% Offset Yield Strength		Ultimate Tensile Strength		Elongation
	°C	°F	mm	in	MPa	ksi	MPa	ksi	%
Sheet	1163	2125	0.6	0.025	372	54.0	752	109.0	61.0
Sheet	1163	2125	2.0	0.079	400	58.0	786	114.0	62.0
Sheet	1163	2125	3.2	0.125	359	52.0	758	110.0	64.0
Plate	1149	2100	4.8	0.188	407	59.0	745	108.0	63.0
Plate	1149	2100	6.4	0.25	393	57.0	731	106.0	63.0
Plate	1149	2100	12.7	0.5	365	53.0	731	106.0	69.0
Plate	1149	2100	25.4	1.0	359	52.0	171	104.0	71.0
Plate	1149	2100	38.1	1.5	331	48.0	696	101.0	76.0
Bar	1149	2100	9.7	0.38	331	48.0	745	108.0	67.0
Bar	1149	2100	19.1	0.75	345	50.0	738	107.0	69.0
Bar	1149	2100	25.4	1.0	379	55.0	758	110.0	68.0
Bar	1149	2100	50.8	2.0	379	55.0	724	105.0	71.0
Bar	1149	2100	88.9	3.5	386	56.0	738	107.0	71.0

Elevated Temperature Tensile Data (Averaged for Plates and Bars)

Temperature		0.2% Offset Yield Strength		Ultimate Tensile Strength		Elongation
°C	°F	MPa	ksi	MPa	ksi	%
93	200	319	46.3	724	105	70.3
149	300	308	44.7	684	99.2	68.8
204	400	283	41	676	98	69.3
260	500	260	37.7	641	93	67.9
316	600	243	35.3	616	89.3	72.7
371	700	234	33.9	605	87.8	69.8
427	800	216	31.3	609	88.3	73
482	900	223	32.4	585	84.9	72.6
538	1000	214	31	586	85	75.3
649	1200	209	30.3	554	80.3	70.7

Charpy V-Notch Impact Data (Plate)

Test Temperature		Condition	Impact Strength
°C	°F		J	ft.lbf
RT	RT	Annealed	>358	>264
-196	-320	Annealed	>358	>264
RT	RT	Annealed then Aged for 100 h at 260°C/500°F	>358	>264
-196	-320	Annealed then Aged for 100 h at 260°C/500°F	342	252
RT	RT	Annealed then Aged for 100 h at 538°C/1000°F	224	165
-196	-320	Annealed then Aged for 100 h at 538°C/1000°F	174	128