Test Temperature		Ultimate Tensile Strength		Yield Strength at 0.2% Offset		Elongation in 2 in (51mm)
°F	°C	Ksi	MPa	Ksi	MPa	%
Room	Room	125.0	860	60.6	420	53.4
200	95	120.7	830	55.3	380	56.9
400	205	110.0	760	47.0	325	59.7
600	315	104.4	720	43.5	300	63.4
800	425	102.0	705	42.4	290	62.0
1000	540	97.8	675	39.0	270	59.0
1200	650	103.5	715	45.8	315	55.8

* Limited data for 0.125" (3.2mm) bright annealed sheet

Tensile Properties, Plate*

Test Temperature		Ultimate Tensile Strength		Yield Strength at 0.2% Offset		Elongation in 2 in (51mm)	Reduction of Area*
°F	°C	Ksi	MPa	Ksi	MPa	%	%
Room	Room	128.3	885	58.2	400	57.8	67.5
200	95	122.4	845	54.1	375	58.2	67.3
400	205	115.1	795	47.6	330	60.9	68.1
600	315	111.2	765	44.4	305	61.6	65.5
800	425	108.2	745	41.3	285	61.7	64.9
1000	540	105.6	730	39.6	275	61.7	61.5
1200	650	106.9	735	42.0	290	64.6	54.9

* Average results for six lots of plate from three heats. Half of the test data are for 1/4-inch (6.3mm) plate, requiring flat test specimens. Rest of samples were round geometry for heavier plate. Thus, reduction of areas reported are for these tests only.

Haynes International, Inc. 800-354-0806 765-456-6012

HASTELLOY® B-3 ® alloy Information*

A nickel-molybdenum alloy with outstanding resistance to hydrochloric and sulfuric acids in the as-welded condition and excellent thermal stability.

HASTELLOY^® B-3 ^® alloy Information*

A nickel-molybdenum alloy with outstanding resistance to hydrochloric and sulfuric acids
in the as-welded condition and excellent thermal stability.